SUNECON TG-8000High performance additive antistatic agent

High performance additive antistatic agent SUNECON TG-8000

By adding or kneading to rubber, resin, etc, it will supress the static electricity to cause.

TG-8000
Name TG-8000
Usages and main applications

SUNECON TG-8000 is a solvent soluble additive antistatic agent excelling the stability over time.

By combing few percent of agent to rubber, adhesive, resin, coating, UV coat, the surface resistance decreases to 1010 acting as high performance antistatic agent.

Specifcation will be as follows.

・antistatic effect excels over time

・antistatic effect excels over time

・colorless

・independent to humidity

・dissolute to various solvent

・available to knead into rubber, resin, etc

・available to combine to adhesive, coating, etc

property(typical value) Appearance colorless~light yellow liquid
Proportion about 1.27 (20℃)
viscosity

about 700 mPa・s(20℃)

Flash point

none

How to use
usage

・when combining to rubber, gradually add TG-8000 and knead until it is mixed.

・When kneading to a resin, combine TG-8000 when making ric master badge.

・When combining to adhesive or coating, mix until TG-8000 is dissoluted.

classification

non-toxic, non-hazardous material

shipping

UN classification: none

UN number: none

①Example of crylic adhesive usage

Coat the antistatic mixed adhesive solution(0,1,3,5%) to a PET film, dry out for 5min in 100℃, and measured the surface resistance. Evaluated the transparency by looking.

SUNECON TG-8000 added amount(Amount compared to solid)Surface resistance(Ω/cm2)Transparency
1.0%2×1011
3.0%1×1010
5.0%1×109
0%(not included)5×1015
②Example of usage to UV coating

Mix until the TG-8000 is dissoluted, and coat to PET film.

SUNECON TG-8000 added amount(Amount compared to solid)Surface resistance(Ω/cm2)
1.0%1×1011
5.0%5×109
0%(not included)1×1016
other surfactant(1.0%)5×1013

In both ①②, the surface resistance was lower than non-applied, and antistatic effect was observed.

  • TAIYO CHEMICALS & 
ENGINEERING CO.,LTD. 2-8-11 Higashi-Nihonbashi, Chuo-ku, Tokyo 103-0004 Japan
  • EQA
  • TEL03-5687-1931 weekday9:00-17:00
  • FAX03-5687-1933 24 hours reception
  • mailContact Us
  • TEL03-5687-1931